Pritidenta ZrO2 Multi Translucent PLUS 16 mm

Description

pritidenta priti multidisc ZrO₂ Multi Translucent PLUS is a pre-shaded gradient zirconia for the fabrication of aesthetic and durable all-ceramic restorations. It combines strong 4Y-TZP in the body region with highly translucent 5Y-TZP in the enamel region, providing a harmonious progression of shade, translucency and strength.

Product facts

• Size: 98.5 × 16 mm
• Type: Pre-shaded multi-translucent gradient zirconia
• Material: Yttria-stabilised zirconium oxide
• Material structure: Combination of 4Y-TZP and highly translucent 5Y-TZP
• Body region: High-strength 4Y-TZP
• Enamel region: Highly translucent 5Y-TZP
• Flexural strength: Typical mean value of at least 1,150 MPa
• Flexural strength in the upper layer: More than 980 MPa
• Flexural strength in the lower layer: More than 1,310 MPa
• Translucency: Gradient from more than 45% to more than 49%
• ISO classification: Type II, class 5 according to DIN EN ISO 6872
• Indications: Veneers, inlays, onlays, partial crowns, crowns, bridges and abutments
• Bridge indication: Restorations of up to 14 units

Benefits

The combination of different zirconia qualities provides high mechanical stability and natural translucency within the same disc. Its gradual strength transition makes the material suitable for a broad range of indications, while the integrated shade and translucency gradient can reduce the need for extensive individual characterisation.

Shade and aesthetics

The material provides a smooth progression from a stronger and more chromatic body region to a lighter and more translucent enamel region. The harmonious gradient is designed for reproducible shade results and reliable matching with the VITA Classical shade guide.

Applications

Suitable for monolithic and anatomically reduced crowns, partial crowns and bridges of up to 14 units. The material can also be used for inlays, onlays, veneers and abutments and is particularly suitable for aesthetically visible regions and anterior restorations.

Processing

The material is supplied in a pre-sintered state and is processed in a compatible dental CAD/CAM system. All common processing techniques can be used, including staining and glazing, cut-back and ceramic veneering. The veneering ceramic must be compatible with the zirconia coefficient of thermal expansion of 10.5 ± 0.5 × 10⁻⁶ K⁻¹. Fast sintering with a total processing time of approximately four hours is possible for approved restorations of up to three units.